Shape memory polymer articles with a microstructured surface

ABSTRACT

A shape memory polymer article is disclosed. The article may include a surface having a microstructure and it may include a shape memory polymer. The shape memory polymer may include a copolymer network. The copolymer network may be formed from the reaction product of a free radically polymerizable siloxane having greater than one functional free radically polymerizable group and at least one (meth)acrylate monomer.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is related to commonly assigned, co-pending U.S. patentapplication Ser. No. ______ by Sherman et al., entitled “Method ofForming and Using Shape Memory Polymer,” and filed of even date herewith(Docket 62183US002); and to commonly assigned, co-pending U.S. patentapplication Ser. No. ______ by Dunn et al., entitled “Microlens SheetingWith Floating Image Using A Shape Memory Material,” and filed of evendate herewith (Docket 62252US002).

FIELD OF THE INVENTION

The invention relates to shape memory polymers, and particularly, toshape memory polymers having microstructured surfaces.

BACKGROUND

Shape memory materials have the unique ability to “remember” a pre-setshape and, upon exposure to the appropriate stimuli, shift from adeformed or altered shape back to the pre-set shape. Severalcommercially important uses have been developed for shape memorymaterials. For example, shape memory metal alloys are commonly used invarious medical, dental, mechanical, and other technology areas for awide variety of products.

Shape memory polymers and the uses of these materials have emerged morerecently. However, the basic premise behind these materials is thesame—that the material can be pre-set in a particular shape, deformed,and then revert back to the pre-set shape when exposed to theappropriate stimuli.

SUMMARY

The present disclosure relates generally to shape memory polymerarticles. The shape memory polymer articles may include amicrostructured surface.

In one embodiment, an illustrative article is described that includes apolymeric member. The polymeric member may include a surface having amicrostructure and it may include a shape memory polymer. The shapememory polymer may include a copolymer network. The copolymer networkmay include the reaction product of a free radically polymerizablesiloxane having greater than one functional free radically polymerizablegroup and at least one (meth)acrylate monomer. The at least one(meth)acrylate monomer, when homopolymerized, may form a homopolymerthat has a glass transition temperature, a melting temperature, or bothgreater than about 40° C.

In another embodiment, an illustrative article is described thatincludes a polymeric member having a microstructured surface. Themicrostructured surface may include a surface feature that is notvisible to an unaided eye. The polymeric member may include a shapememory polymer.

In yet another embodiment, an illustrative article is described thatincludes a polymeric member having a microstructured surface. Themicrostructured surface may include a surface feature that is notvisible to an unaided eye. The polymeric member may include a shapememory polymer. The shape memory polymer may include a copolymernetwork. The copolymer network may include the reaction product of(meth)acryloxyurea siloxane and isobornyl acrylate.

The above summary of the present invention is not intended to describeeach disclosed embodiment or every implementation of the presentinvention. The Figures, Detailed Description and Examples, which follow,more particularly exemplify these embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention may be more completely understood in consideration of thefollowing detailed description of various embodiments of the inventionin connection with the accompanying drawings, in which:

FIG. 1 is a side view of an illustrative article having a surface with amicrostructure;

FIG. 2 is a side view of another illustrative article having a surfacewith a microstructure; and

FIG. 3 is an alternative side view of the illustrative article shown inFIG. 2.

While the invention is amenable to various modifications and alternativeforms, specifics thereof have been shown by way of example in thedrawings and will be described in detail. It should be understood,however, that the intention is not to limit the invention to theparticular embodiments described. On the contrary, the intention is tocover all modifications, equivalents, and alternatives falling withinthe spirit and scope of the invention.

DETAILED DESCRIPTION

Generally, this disclosure is directed to shape memory polymer articlesthat have a microstructured surface. While the present invention is notso limited, an appreciation of various aspects of the invention will begained through discussion of the various features and componentsprovided below.

Selected Definitions

All numeric values are herein assumed to be modified by the term“about,” whether or not explicitly indicated. The term “about” generallyrefers to a range of numbers that one of skill in the art would considerequivalent to the recited value (i.e., having the same function orresult). In many instances, the terms “about” may include numbers thatare rounded to the nearest significant figure.

Weight percent, percent by weight, wt %, wt-%, % by weight, and the likeare synonyms that refer to the concentration of a substance as theweight of that substance divided by the weight of the composition andmultiplied by 100.

The recitation of numerical ranges by endpoints includes all numberssubsumed within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3,3.80, 4, and 5).

As used in this specification and the appended claims, the singularforms “a”, “an”, and “the” include plural referents unless the contentclearly dictates otherwise. As used in this specification and theappended claims, the term “or” is generally employed in its senseincluding “and/or” unless the content clearly dictates otherwise.

As used herein, the term “alkyl” refers to a straight or branched chainmonovalent hydrocarbon radical optionally containing one or moreheteroatomic substitutions independently selected from S, O, Si, or N.Alkyl groups generally include those with one to twenty atoms. Alkylgroups may be unsubstituted or substituted with those substituents thatdo not interfere with the specified function of the composition.Substituents include alkoxy, hydroxy, mercapto, amino, alkyl substitutedamino, or halo, for example. Examples of “alkyl” as used herein include,but are not limited to, methyl, ethyl, n-propyl, n-butyl, n-pentyl,isobutyl, and isopropyl, and the like.

As used herein, the term “aryl” refers to monovalent unsaturatedaromatic carbocyclic radicals having a single ring, such as phenyl, ormultiple condensed rings, such as naphthyl or anthryl. Aryl groups maybe unsubstituted or substituted with those substituents that do notinterfere with the specified function of the composition. Substituentsinclude alkoxy, hydroxy, mercapto, amino, alkyl substituted amino, orhalo, for example. Such an aryl ring may be optionally fused to one ormore of another heterocyclic ring(s), heteroaryl ring(s), aryl ring(s),cycloalkenyl ring(s), or cycloalkyl rings. Examples of “aryl” as usedherein include, but are not limited to, phenyl, 2-naphthyl, 1-naphthyl,biphenyl, 2-hydroxyphenyl, 2-aminophenyl, 2-methoxyphenyl and the like.

As used herein the term (meth)acrylate is used to define both acrylatesand methacrylates.

The term telechelic siloxane refers to siloxanes with 2 reactive groups,one at either end of the siloxane chain.

As used herein, the term shape memory polymer refers to polymericmaterials that are stimuli-responsive. Upon application of an externalstimuli they have the ability to change their shape. A change in shapeinitiated by a change in temperature can be referred to as a thermallyinduced shape memory effect. While not being bound by theory, the shapememory effect may result from the polymer's structure, that is, itsmorphology in combination with a certain processing and programmingtechnology. Therefore, the shape-memory behavior can be observed forseveral polymers that may differ significantly in their chemicalcomposition.

Articles

The present disclosure is directed to articles. The articles may includea polymeric member that has a surface with a microstructure and thatincludes a shape memory polymer. The articles contemplated span a vastarray of technical fields and include essentially any structure that mayfind utility or otherwise benefit from having a shape memory polymerincorporated into their construction. This may include a variety ofdifferent devices, apparatuses, components or portions of devices,layers or surfaces on devices, and the like, or any other suitablestructure. For example, the articles of this disclosure may include anadhesive, a tape or substrate including an adhesive, a heat-activatedtape, a microstructured tape, a backing member, a foam tape, a devicehaving a fluid disposed or encapsulated therein, a microfluidic device,a circuit or circuit board, a printed circuit, a film (includingmultilayer optical films), a micromachined article, an embossed article,a printing plate or film used to create 3D prints, a substrate forpattern coating and/or pattern printing, an electrode, a device havingcube corners with retroreflective characteristics, a secureidentification article, a secure license or license plate, a directionalorganic light emitting diode, a sensor, an indicator, a switch, and thelike, or any other suitable device. It should be noted that this list ofarticles is not intended to be limiting as the articles contemplated cantake the form of any suitable structure, apparatus, or device.

As indicated above, an exemplary article may include a shape memorypolymer. Some examples of shape memory polymers suitable for thearticles are described in more detail below. In some embodiments, theentire article is made from the shape memory polymer. In otherembodiments, only a portion of the article is made from a shape memorypolymer. This may include a shape memory polymer layer, a shape memorypolymer surface, a shape memory polymer portion, or any other suitableconfiguration. When only a portion of the article is made from a shapememory polymer, the remaining materials making up the article mayinclude metals, metal alloys, polymers, ceramics, and the like, or anyother suitable material. Regardless of whether the article is completelyor partially made from a shape memory polymer, the articles describedherein can be described as “shape memory polymer articles”.

Shape memory polymers are known to have the unique ability to be set ina pre-set shape, deformed to an altered shape, and then revert back tothe pre-set shape when exposed to the appropriate stimuli (e.g., changesin temperature, application of solvent, etc.). Because the articlesdisclosed herein include a shape memory polymer, the portion of thearticle (or all of the article if made completely from a shape memorypolymer) having the shape memory polymer can be configured to utilizethis property. For example, the article may include a shape memorypolymer surface that has been cast or otherwise shaped to have a pre-setshape or configuration. This surface can be deformed to an altered ordeformed shape and then be shifted back to the pre-set shape whenappropriately cued. Triggering the shift from the deformed shape to thepre-set shape can vary depending on the particular polymer used or otherparameters. However, at least some of the shape memory polymersdisclosed herein can be shifted by exposure to elevated temperaturesand/or to an appropriate solvent.

Also as indicated above, the articles include a surface having amicrostructure. Generally, a surface with a microstructure is differentthan a “flat” or unstructured surface. As used herein, the term“microstructure” means the configuration of features wherein at least 2dimensions of the features are microscopic. The topical and/orcross-sectional view of the features, therefore, are microscopic. Asused herein, the term “microscopic” refers to features of small enoughdimension so as to require an optic aid to the naked eye when viewedfrom any plane of view to determine its shape. One criterion is found inModern Optic Engineering by W. J. Smith, McGraw-Hill, 1966, pages104-105 whereby visual acuity,“ . . . is defined and measured in termsof the angular size of the smallest character that can be recognized.”Normal visual acuity is considered to be when the smallest recognizableletter subtends an angular height of 5 minutes of arc on the retina. Ata typical working distance of 250 mm (10 inches), this yields a lateraldimension of 0.36 mm (0.0145 inch) for this object.

The microstructures may be formed along portions or all of any number ofsurfaces of the article. For example, some surfaces of the articles mayinclude sections that have microstructures and sections that are freefrom microstructures. Alternatively, substantially all of one or moresurfaces of the articles may include microstructures. In addition, theshape and/or configuration of the microstructures can also vary. Forexample, microstructures can include one or more projections, one ormore depressions, a combination of projections and depressions, ridges,posts, pyramids, hemispheres, cones, protrusion, or any other suitablefeature. The shapes of the various projections and/or depressions canalso vary. For example, some embodiments of projections and/ordepressions can be rounded in shape (e.g., circular, semicircular,spherical, hemispherical, oval, pill-shaped, partially pill-shaped,etc.) or include a rounded portion, polygonal in shape or include apolygonal portion (e.g., triangular, squared, cubed including cubecorners, tetrahedrical, rectangular, paralleopiped, pentagonal,hexagonal, etc.), an irregular shape, a regular shape, a pointed shape,a truncated shape, combinations thereof, or any other suitable shape. Inat least some of these as well as in other embodiments, the projectionsand/or depressions may include or define one or more channels, valleys,wells, ridges, and the like, combinations thereof, or any otherconfiguration.

Microstructures may be formed in a surface of an article through the useof a microstructured molding tool. A microstructured molding tool is animplement for imparting a structure or finish to at least a portion ofan article and that may be continuously reused in the process.Microstructured molding tools can be in the form of a planar stampingpress, a flexible or inflexible belt, a roller, or the like.Furthermore, microstructured molding tools are generally considered tobe tools from which the microstructured surface feature is generated byembossing, coating, casting, or platen pressing and do not become partof the finished microstructured article. Instead, a surface on thearticle corresponding to where the article came into contact with themicrostructured surface of the molding tool defines the microstructureor microstructured surface feature of the article.

A broad range of methods are known to those skilled in this art forgenerating microstructured molding tools. Examples of these methodsinclude but are not limited to photolithography, etching, dischargemachining, ion milling, micromachining, and electroforming.Microstructured molding tools can also be prepared by replicatingvarious microstructured surfaces, including irregular shapes andpatterns, with a moldable material such as those selected from the groupconsisting of crosslinkable liquid silicone rubber, radiation curableurethanes, etc. or replicating various microstructures by electroformingto generate a negative or positive replica intermediate or finalembossing tool mold. Also, microstructured molds having random andirregular shapes and patterns can be generated by chemical etching,sandblasting, shot peening or sinking discrete structured particles in amoldable material. Additionally any of the microstructured molding toolscan be altered or modified according to the procedure taught in U.S.Pat. No. 5,122,902, the entire disclosure of which is hereinincorporated by reference.

For illustration purposes, FIG. 1 is provided to depict a portion of anexample article 10. Article 10 includes a shape memory polymer such as,for example, any of the shape memory polymers described herein. Article10 may comprise a polymeric member that includes a surface 12 having aplurality of surface features or microstructures 14 formed therein. Inthis example, microstructures 14 are depicted as projections extendingoutward from surface 12. However, this arrangement is not intended to belimiting as a wide variety of differing arrangements are contemplatedincluding those described above.

Depending on the application, article 10 may be in the “pre-set” shapeor may be in the “deformed” shape. If article 10, as shown in FIG. 1, isin the pre-set shape, surface 12 can be deformed. This may beaccomplished, for example, by changing the configuration ofmicrostructures 14. For example, microstructures 14 may be flattened.The deformed article 10 can be shifted back to the pre-set configuration(i.e., the configuration depicted in FIG. 1 for this example) uponexposure to, for example, increased temperature, solvent, or any othersuitable stimuli. Alternatively, if article 10 is in the deformed shapeor configuration when arranged as shown in FIG. 1, exposure to theappropriate stimuli may shift article 10 back to the pre-set shape. Inthis later embodiment, the pre-set shape may include a generally flat orplanar arrangement for surface 12 or any other suitable shape.

FIGS. 2-3 depict another example article 1010. Article 1010 maycomprise, a sensor. In this embodiment, article 1010 may include asurface 1012 having a microstructure defined therein. The microstructuremay include, for example, a plurality of rows or wells 1014. Thisconfiguration may be the pre-set shape of surface 1012. Surface 1012 canbe deformed into a deformed shape that is, for example, substantiallyflat. A secondary surface 1012′, for example on the opposite side ofarticle 1010 (which is indicated in FIG. 3 as article 1010′) may have agenerally flat pre-set shape that can be deformed to have amicrostructure that includes or defines a hexagonal pattern therein.Mobilizing may restore both surfaces 1012/1012′. For example, surface1012 may shift back to the pre-set shape (see FIG. 2) and oppositesurface 1012′ may shift back to a substantially flat shape. In thisembodiment, mobilizing may include the application of heat and/or theexposure to solvent or solvent vapors to one or both of surface 1012and/or surface 1012′. For example, surfaces 1012/1012′ may be exposed toheat and restored. Alternatively, surfaces 1012/1012′ may be exposed tosolvent or solvent vapors. This later embodiment may allow article 1010to be used as a sensor that can “smell” a solvent. For example, a usermay visually observe the changes in the shape of article 1010 (on one orboth sides) in order to observe that the sensor has smelled a particularsolvent.

FIGS. 2-3, in addition to illustrating that article 1010 can be used asa sensor, also indicate that a surface having a pre-set shape may beformed on multiple sides of an article. For example, FIGS. 2-3illustrate article 1010 having surface 1012 with a pre-set shape thatincludes a microstructure whereas surface 1012′ has a pre-set shape thatis generally planar. In these embodiments or embodiments of the samespirit, one or both of the surfaces 1012/1012′ can be deformed. Forexample, surface 1012 can be flattened whereas surface 1012′ can bedeformed to have a microstructure. Thus, article 1010 can be seen ashaving a secondary surface 1012′ with a microstructure. It can beappreciated that secondary surface 1012′ may, alternatively, have apre-set shape that includes the microstructure shown in FIG. 3 and itcan be deformed to have another shape. Moreover, the secondary surface1012′ (or other surfaces having a pre-set shape) may be defined alongany area of the article 1010 and need not be limited to just a surfacethat is opposite of surface 1012. Regardless of the configuration ofsurfaces 1012/1012′, mobilization shifts surfaces 1012/1012′ back totheir pre-set shape. It can be appreciated that other articles arecontemplated that have multiple surfaces with pre-set shapes includingmultiple planar surfaces and/or multiple surfaces with microstructures.Moreover, other embodiments are contemplated where one or more surfaceshave a microstructure formed therein and one or more of these surfacescan be deformed to have a different microstructure.

Shape Memory Polymers

As described above, the articles disclosed herein include a shape memorypolymer. Shape memory polymers can be classified as elastomers. On themolecular level they represent polymer networks that include segmentchains that are connected by netpoints. The netpoints can be formed byentanglements of the polymer chains or intermolecular interaction ofcertain polymer blocks. These cross-links are called physical netpoints.Cross-links in the form of covalent bonds form chemical netpoints. Anelastomer exhibits a shape-memory functionality if the material can bestabilized in the deformed state in a temperature range that is relevantfor the particular application. This can be achieved by using thenetwork chains as a kind of molecular switch. For this purpose, itshould be possible to limit the flexibility of the segments as afunction of temperature. This process is supposed to be reversible. Theability to incorporate a control function into the material provides athermal transition T_(trans) of the network chains in the temperaturerange of interest for the particular application. At temperatures aboveT_(trans) the chain segments are flexible, whereas the flexibility ofthe chains below this thermal transition is at least partially limited.In the case of a transition from the rubber-elastic, i.e., viscous, tothe glassy state the flexibility of the entire segment is limited.

Without being bound to theory, it is believed that the copolymer networkincludes an elastomeric phase or component and a “glassy” or high glasstransition temperature phase or component. The glassy phase holds orconstrains the elastomeric component so that the substrate can bedeformed into and stays in the deformed shape. Shifting from a deformedshape to the pre-set shape generally includes mobilizing the glassyphase of the shape memory polymer in order to allow the elastomericcomponent to “spring back” or otherwise shift to the original pre-setshape. According to this theory, mobilizing is understood to be themobilization of the glassy phase through the application of theappropriate external stimuli.

In at least some embodiments, the elastomeric phase comprises a freeradically polymerizable siloxane having greater than one functional freeradically polymerizable group. The glassy phase may comprise at leastone (meth)acrylate monomer that, when homopolymerized, forms ahomopolymer having a glass transition temperature, a meltingtemperature, or both greater than about 40° C. According to theseembodiments, exposure of the shape memory polymer to temperaturesgreater than 40° C. can mobilize the glassy phase and cause the deformedsurface of the substrate from the deformed shape to the pre-set shape.In other embodiments, a solvent such as alkyl alcohol, acetone, etc. canpartially dissolve or plasticize the glassy phase and effectuate thesame change. In some embodiments, the (meth)acrylate monomer maycrystallize when reacted with the free radically polymerizable siloxanehaving greater than one functional free radically polymerizable group.In these embodiments, exposing the copolymer network to temperaturesabove the melting point of the (meth)acrylate monomer may mobilize theglassy phase.

The relative proportions of the various components of the copolymernetwork can vary. For example, in at least some embodiments, thecopolymer network may include about 10-70 weight-percent of the freeradically polymerizable siloxane. In other embodiments, the copolymernetwork may include about 10-60 weight-percent of the free radicallypolymerizable siloxane. In still other embodiments, the copolymernetwork may include about 20-60 weight-percent of the free radicallypolymerizable siloxane.

Free Radically Polymerizable Siloxanes

The free radically polymerizable siloxanes for use in the copolymernetworks may be represented by the following formula:

wherein:

X is a group having ethylenic unsaturation;

Y is a divalent linking group;

m is an integer of 0 to 1;

D is selected from the group consisting of hydrogen, an alkyl group of 1to about 10 carbon atoms, aryl, and substituted aryl;

R is a divalent hydrocarbon group;

R₁ are monovalent moieties which can be the same or different selectedfrom the group consisting of alkyl, substituted alkyl, aryl, andsubstituted aryl;

R₂ are monovalent moieties which can be the same or different selectedfrom the group consisting of alkyl, substituted alkyl, aryl, andsubstituted aryl;

R₃ are monovalent moieties which can be the same or different selectedfrom the group consisting of alkyl, substituted alkyl, vinyl, aryl, andsubstituted aryl;

R₄ are monovalent moieties which can be the same or different selectedfrom the group consisting of alkyl, substituted alkyl, vinyl, aryl, andsubstituted aryl; and

n is an integer of about 10 to about 2000.

Some examples of suitable free radically polymerizable siloxanes for usein the articles described herein may include those described in U.S.Pat. No. 5,091,483, the entire disclosure of which is hereinincorporated by reference.

In at least some embodiments, the free radically polymerizable siloxanescomprise telechelic siloxanes. The telechelic siloxanes may include, forexample, (meth)acryloxyurea siloxane (MAUS), acrylamidoamido siloxane(ACMAS), methacrylamidoamido siloxane (MACMAS), and methylstyrylureasiloxane (MeStUS). In general, these telechelic siloxanes are formed byreacting silicone diamines with capping reagents such asisocyanatoethylmethacrylate (IEM), vinyldimethylazlactone (VDM),isopropenyl dimethyl azlactone (IDM), and m-isopropenyl alpha,alpha-dimethyl benzyl isocyanate (m-TMI), respectively. These telechelicsiloxanes may have a number average molecular weights in the range ofabout 1,000 to 200,000. Some additional details regarding synthesis isprovided below. Particularly preferred telechelic siloxanes are thosethat include a polydimethylsiloxane chain and may also be referred to aspolydimethylsiloxanes.

The telechelic siloxanes have free radically polymerizable end groups.Due to the polar nature of the hydrogen bonding end groups and thenonpolar nature of the polydimethylsiloxane chain, a transient networkis formed wherein the polar end groups tend to associate with eachother. The relative strength of the end group association for thevarious telechelic siloxanes is reflected in their viscosities, withhigher viscosities seen in the case of the more strongly associating endgroups (e.g., ACMAS and MeStUS).

Functional polymers, like these telechelic siloxanes, that are easy tocure to elastomers are often referred to as “liquid rubbers.” Indeed, bythe exposure of telechelic siloxanes having free radically polymerizableend groups to low-intensity UV radiation (when the system containsphotoinitiator), silicone elastomers with controlled properties can beobtained.

In general the telechelic siloxanes are obtained from amine-functionalsiloxane intermediates. Suitable polydiorganosiloxane diamines andmethods of making the polydiorganosiloxane diamines are described, forexample, in U.S. Pat. No. 3,890,269 (Martin), U.S. Pat. No. 4,661,577(Jo Lane et al.), U.S. Pat. No. 5,026,890 (Webb et al.), U.S. Pat. No.5,276,122 (Aoki et al.), U.S. Pat. No. 5,214,119 (Leir et al.), U.S.Pat. No. 5,461,134 (Leir et al.), U.S. Pat. No. 5,512,650 (Leir et al.),and U.S. Pat. No. 6,355,759 (Sherman et al.), incorporated herein byreference in their entirety. Some polydiorganosiloxane diamines arecommercially available, for example, from Shin Etsu Silicones ofAmerica, Inc., Torrance, Calif. and from Gelest Inc., Morrisville, Pa.Particularly useful polydiorganosiloxane diamines includebis(3-aminopropyl)polydimethylsiloxanes.

Polydimethylsiloxanes having acrylamidoamido end groups (ACMAS) can beprepared by the reaction of a polydimethylsiloxane diamine with 2equivalents of vinyl dimethyl azlactone (VDM). Similarly,polydimethylsiloxanes having methacrylamidoamido end groups (MACMAS) canbe prepared in the same manner by the reaction of a polydimethylsiloxanediamine with 2 equivalents of isopropenyl dimethyl azlactone (IDM).

Polydimethylsiloxanes having methacryloxyurea end groups (MAUS) can beprepared using the same procedure, by the reaction of apolydimethylsiloxane with 2 equivalents of isocyanatoethyl methacrylate(IEM).

Polydimethylsiloxanes having alpha-methylstyrylurea end groups (MeStUS)can be made by the reaction of a polydimethylsiloxane with 2 equivalentsof m-isopropenyl-alpha,alpha-dimethyl benzyl isocyanate (m-TMI).

In other embodiments the free radically polymerizable siloxanes comprisenon-techelic siloxanes. These siloxanes are ones according to the aboveformula where at least some of the groups R₃ and/or R₄ comprise vinylgroups.

(Meth)Acrylate Monomers

Generally, (meth)acrylate monomers are monomers that are the(meth)acrylate esters of non-tertiary alkyl alcohols, the alkyl groupsof which comprise from about 1 to about 20, or about 1 to about 18carbon atoms. Suitable (meth)acrylate monomers include, for example,benzyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, ethylmethacrylate, isobornyl acrylate, isobornyl methacrylate, methylmethacrylate, 1-methylcyclohexyl methacrylate, 2-methylcyclohexylmethacrylate, 3-methylcyclohexyl methacrylate, 4-methylcyclohexylmethacrylate, and 2-phenoxy ethyl methacrylate.

Particularly suitable (meth)acrylate monomers are those that, whenhomopolymerized, form a homopolymer having a glass transitiontemperature, a melting temperature, or both greater than about 40° C.These monomers are suitable in forming a copolymer network with a freeradically polymerizable siloxane. Examples of preferred (meth)acrylatemonomers include isobornyl acrylate, cyclohexyl acrylate, trimethylcyclohexyl acrylate, methyl methacrylate, methacrylic acid, t-butylacrylate. A single (meth)acrylate monomer or a combination of(meth)acrylate monomers may be used.

The glass transition temperature (and/or the melting temperature) may bemeasured by conventional techniques such as Differential ScanningCalorimetry (DSC) or Dynamic Mechanical Analysis (DMA). Some additionaldetails regarding these components of the copolymer network aredescribed in more detail below.

Curing Initiator

As indicated above, the shape memory polymer may be a copolymer networkincluding the reaction product of a free radically polymerizablesiloxane having greater than one functional free radically polymerizablegroup and at least one (meth)acrylate monomer. The reaction may include,for example, polymerization via curing. Curing may be carried out in anoxygen-free, e.g., in an inert atmosphere such as nitrogen gas or byutilizing a barrier of radiation-transparent material having low oxygenpermeability. Curing can also be carried out under an inerting fluidsuch as water. When visible or ultraviolet radiation is used for curing,the reaction may also contain a photoinitiator. Suitable photoinitiatorsinclude benzoin ethers, benzophenone and derivatives thereof,acetophenone derivatives, camphorquinone, and the like. Some examples ofcommercially available photoinititaors include DARACUR 1173, DAROCUR4265, IRGACURE 651, IRGACURE 1800, IRGACURE 369, IRGACURE 1700, andIRGACURE 907, commercially from Ciba Geigy. The photoinitiator may beused at a concentration of from about 0.1% to about 5% by weight of thetotal polymerizable composition, and, if curing is carried out under aninerting fluid, the fluid is preferably saturated with thephotoinitiator or photoinitiators being utilized in order to avoid theleaching of initiator from the reaction. The rapid cure observed forthese materials allows for the use of relatively low levels ofphotoinitiator, hence uniform cure of thick sections can be achieved dueto deeper penetration of radiation. If desired, curing can also beachieved thermally, which may include the use of thermal initiator suchas peroxides, azo compounds, or persulfates generally at a concentrationof from about 1% to about 5% by weight of the total polymerizablecomposition. In at least some embodiments, any initiator (thermal orphoto-) utilized may be soluble in the reaction components themselves,thereby avoiding the need for a separate solvent. Liquid initiators maybe preferred.

Preparation of Silicone-Acrylate Copolymeric Networks

Polymerization mixtures can be prepared by dissolving telechelicsiloxanes in the (meth)acrylate monomers and adding a photoinitiatorSuch polymerization mixtures typically have viscosities that permit thepreparation of samples in film form by direct coating and radiationcuring by standard procedures.

The shape memory polymer article may be formed by coating and curing thepolymerizable mixture in a structured configuration, by curing thepolymerization mixture in an unstructured configuration and thenapplying a structure through the imposition of heat and pressure, or bya combination of the these processes.

For example, the polymerization mixture can be coated onto a carrierlayer such as a liner (either structured or unstructured), onto asubstrate (such as a metal sheet or foil, a film, a ceramic or piece ofglass, etc) or onto a tool or mold. The coated polymerization mixture isthen covered with a covering layer which may be another liner,substrate, tool or mold and may be the same or different from thecarrier layer. The resulting construction is then cured, preferably withUV radiation. Upon curing one or both of the carrier layer and or thecovering layer are removed and the shape memory polymer article may thenbe subjected to additional processing (to create or remove structuring,to form in articles of a desired shape, etc).

The entire disclosures of the following patents, which are referred toin the various Examples, are herein incorporated by reference: U.S. Pat.No. 5,514,730, U.S. Pat. No. 5,706,132, and U.S. Pat. No. 6,569,521.

EXAMPLES

These examples are merely for illustrative purposes only and are notmeant to be limiting on the scope of the appended claims. All parts,percentages, ratios, etc. in the examples and the rest of thespecification are by weight, unless noted otherwise. Solvents and otherreagents used were obtained from Sigma-Aldrich Chemical Company;Milwaukee, Wis. unless otherwise noted.

Table of Abbreviations Abbreviation or Trade Designation Description  5KMAUS Methacryloxyurea siloxane, a difunctional silicone acrylateprepared from PDMS diamine 5K as described in U.S. Pat. No. 5,514,730column 14 for 35K MAUS, using 5,000 g/mole PDMS diamine instead of35,000 g/mole PDMS diamine. PDMS Polydimethyl siloxane DAROCURPhotoinitiator: 2-hydroxy-2-methyl-1-phenyl-propan-1-one from Ciba 1173Specialty Chemicals, Hawthorne, NY. PET Unprimed polyester film ofpolyethylene terephthalate having a thickness of 50 or 125 micrometers. 5K MeStUS Alpha-methyl styrylurea siloxane, a difunctional siliconealpha-methyl styrene prepared from PDMS diamine 5K as described in U.S.Pat. No. 5,514,730 column 14 for 35K MeStUS, using 5,000 g/mole PDMSdiamine instead of 35,000 g/mole PDMS diamine.  5K ACMAS Acrylamidoamidosiloxane, a difunctional silicone acrylamido prepared from PDMS diamine5K as described in U.S. Pat. No. 5,514,730 column 14 for 35K ACMAS,using 5,000 g/mole PDMS diamine instead of 35,000 g/mole PDMS diamine.50K MAUS Methacryloxyurea siloxane, a difunctional silicone acrylateprepared from PDMS diamine 50K as described in U.S. Pat. No. 5,514,730column 14 for 35K MAUS, using 50,000 g/mole PDMS diamine instead of35,000 g/mole PDMS diamine. 50K MeStUS Alpha-methyl styrylurea siloxane,a difunctional silicone alpha-methyl styrene prepared from PDMS diamine50K as described in U.S. Pat. No. 5,514,730 column 14 for 35K MeStUS,using 50,000 g/mole PDMS diamine instead of 35,000 g/mole PDMS diamine.50K ACMAS Acrylamidoamido siloxane, a difunctional silicone acrylamidoprepared from PDMS diamine 50K as described in U.S. Pat. No. 5,514,730column 14 for 35K ACMAS, using 50,000 g/mole PDMS diamine instead of35,000 g/mole PDMS diamine. Water-borne Acrylate polymer dispersion at40% solids. PSA

Example 1

A curable precursor solution of 40 parts of 5K MAUS dissolved in 60parts of IBA, containing 0.5 wt % DAROCUR 1173 was poured on the firsttool, which was an unstructured PET film laid down on the surface of aglass plate. The first tool was bordered by a compliant adhesive film of3 millimeters thickness to serve as a dam for the curable adhesiveprecursor as well as a spacer to control the thickness of the curedfilm. The liquid layer of curable precursor was covered with a coversheet (an unstructured UV transparent film) and the excess fluid wassqueezed out by placing a rigid glass plate over the cover sheet andpressing the thus formed sandwich construction until the glass platerested against the spacer. The sandwich construction was exposed to lowintensity UV lights through the cover sheet for 10-15 minutes. Theresulting cured film (slab) had two surfaces replicated from the firsttool and from the cover sheet (second tool) and was removed from boththe first tool and from the cover sheet. The edges of the substrate weretrimmed.

Example 2

The slab prepared in Example 1 was deformed by pressing against thestructured surface of the metal tool and a polished steel plate withheat/pressure (110° C. for 10 minutes, pre-press 4.1 MegaPascals (600lbs/in²) for 10 minutes, 30 MegaPascals (2 ton/in²) high pressure for 10minutes) and quenched (25 minutes until temperature reached 60° C.). Thestructure of the tool—an array of tilted triangular prisms withmillimeter-size dimensions, was partially replicated—approximately60-70% of the height of the pyramid.

Example 3

A part of the film made in Example 2 was heated to approximately 110° C.on a heating plate. The area exposed to heat became essentially flat,with some traces of the embossed microstructure still visible.

Example 4

A shape-memory substrate was prepared as described in Example 2. Onepart of the sample was submitted to a secondary process of shaving offthe temporary surface features. When the sample was heated to 120° C.the portion of the sample with shaved-off material showed roundedcavities with topologies corresponding to the shaved-off elements.

Example 5

A shape-memory substrate was prepared as described in Example 1 exceptthat the first tool was a microstructured film having linear array ofrectangular channels (200 micrometers at the bottom, 100 micrometers atthe top, 200 micrometer high) and a 1 millimeter spacer was used. Thesample was flattened between the two polished steel plates under theconditions as described in Example 2 except flat tools were used. Onepart of the film was sprayed with metallic silver paint to form a thinlayer of metallic silver. The electrical conductivity of the sample waschecked using a Fluke 87 III RMS Multimeter, which was independent ofthe position of the electrodes (x and y conductive). A portion of thesample was heated to 120° C. on a heating plate to restore the originalshape of the surface. Electrical conductivity of the sample was againchecked. While the sample maintained the electrical conductivity alongthe channels the conductivity in the cross-direction was primarilydestroyed and/or disrupted.

Example 6

A shape-memory substrate was made as described in Example 1 except thatthe first tool was a metal tool with structured surfaces as described inExample 2. The substrate having sharp macroscopic features wassubsequently submitted to heat and pressure between two polished steelplates under the conditions described in Example 2 except flat toolswere used. The substrate became essentially flat with the pyramids beingpartially flattened and partially bent. Part of the original structurewas restored by selectively focusing sunlight through a lens ontoseveral of the pyramids.

Example 7

A shape-memory substrate was tested through the stages of making,distorting and restoring. The sample was made as described in Example 1except that the first tool was a metal tool having an array of cubecorners as described in U.S. Pat. No. 5,706,132. The pyramids had aheight of 87 micrometers (3.5 mil). The spacer used was 125 micrometers.The sample was removed from the first tool while maintained on the flatPET cover. The sample showed retroreflectivity when analyzed using aretroviewer (the sample “made” stage). A part of the sample wasflattened between the two polished steel plates under the conditionsdescribed in Example 2 except that the tools were flat. It was noticedthat the height of the pyramids were reduced, but the pyramidal shape ofthe flattened microfeatures was maintained (the sample “distorted”stage). The sample showed no retroreflectivity in a retroviewer. Aportion of the sample was heated to 120° C., which restored the originalshape of the pyramids and the retroreflectivity of the sample (thesample “restored” stage).

Example 8-13

A series of samples were made, distorted and restored as in Example 7except that different compositions of the curable precursors were used(containing Monomer 1, IBA and DAROCUR 1173) as shown in Table 1.Results of the testing are shown in Table 2.

TABLE 1 Monomer 1 Monomer 1 IBA DAROCUR 1173 Example Identity (parts)(parts) (wt %) 8  5K MeStUS 50 50 0.5 9  5K MAUS 50 50 0.5 10  5K ACMAS50 50 0.5 11 50K MeStUS 50 50 0.5 12 50K MAUS 50 50 0.5 13 50K ACMAS 5050 0.5

TABLE 2 Appearance Sample Appearance As After Appearance Example ColorMade Distortion Distortion As Restored 8 Clear Retroreflective Flattenedto No retroreflection Retroreflective Cubes 0.6 Cubes micrometers 9Clear Retroreflective Flattened to No retroreflection RetroreflectiveCubes 1.0 Cubes micrometers 10 Bluish Retroreflective Flattened to Noretroreflection Retroreflective Haze Cubes 2.0 Cubes micrometers 11Clear Retroreflective Flattened to No retroreflection RetroreflectiveCubes 1.0 Cubes micrometers 12 Clear Retroreflective Flattened to Noretroreflection Retroreflective Cubes 1.5 Cubes micrometers 13 ClearRetroreflective Flattened to No retroreflection Retroreflective Cubes7.8 Cubes micrometers

Example 14

A shape-memory substrate was made as described in Example 1 except thata 125 micrometers spacer was used. One of the surfaces of the substratewas deformed by pressing the sample between the metal tool, havingregularly arranged square posts (150 micrometers at the bottom, 150micrometers at the top, 50 micrometers high), to create a correspondingarray of microcavities. The substrate was coated with a Water-borne PSA.Upon drying the water at 25° C. for 24 hours, the film contained PSAdistributed within the pockets of microstructure substrate and showedno/little tack. A portion of the sample was heated to 120° C. on aheating plate causing the restoration of the original flatness of thesubstrate and making the sample tacky by exposing the PSA layer on thesurface.

Example 15

A shape-memory substrate was made as described in Example 1 except thata 1 millimeter spacer was used. One of the surfaces of the substrate wasdeformed by pressing the sample between the metal tool, having an arrayof triangular posts (420 micrometers depth), to create an array ofvisible cavities. The substrate was flooded with colored aqueous fluidto fill the cavities. Silicone pressure sensitive adhesive tape (asdescribed in U.S. Pat. No. 6,569,521, Example 28) was laminated to thesubstrate to seal off the cavities filled with the fluid. When heated to120° C. the substrate returned to its original shape exerting pressureon the laminated tape causing the tape to also distort, and causing theadhesive border seals to rupture.

Example 16

A shape-memory substrate was made as described in Example 1, except thatthe first tool was a metal tool, a replica of the tool used to deformthe substrate in Example 14, having regularly arranged square cavities(150 micron at the bottom, 150 micron at the top, 45 micrometer high)and a 1 millimeter spacer to create a corresponding array ofmicro-posts. The sample was flattened between two polished steel platesunder the conditions as described in Example 2. The sample was heated to120° C. on a heating plate to restore the original structure (posts) ofthe surface. The posts were able to pick up water-based ink for transferto paper.

Example 17

A shape-memory substrate was made as described in Example 1 except thata 125 micrometers spacer was used. One of the surfaces of the substratewas deformed by pressing the sample between the metal tool havingregularly arranged square posts, as described in Example 14, to create acorresponding array of micro-cavities. When a droplet of the solution ofdye (bromothymol blue, sodium salt) in ethylene glycol was deposited onthe surface of the film, clear-cut borders along the line of the patternwere naturally established, and the solvent essentially restored the“printed” area to flatness with the clearly visible high concentrationof the dye in the spots corresponding to the arrangement of cavities inwhich it was originally deposited.

Example 18

A shape-memory substrate was made as described in Example 1 except thata 125 micrometers spacer was used and the first tool was a metal toolwith an array of square posts, as described in Example 14. The curedsample was pressed between 2 flat surfaces using the technique describedin Example 2. When a droplet of the solution of dye (bromothymol blue,sodium salt) in ethylene glycol was deposited on the surface of thefilm, clear-cut borders along the line of the pattern were naturallyestablished, and the solvent essentially restored the “printed” area toits micro-cavitated form dragging the ink into the cavities.

Examples 19

A shape-memory substrate was made as described in Example 1 except thata 125 micrometers spacer was used. One of the surfaces of the curedsubstrate was deformed by pressing the sample between the metal tool,used in Example 16. A droplet of the aqueous solution of dye(bromophenol blue indicator solution) was deposited and pressed on themicrostructured surface of the shape-memory substrate. The solution wasprimarily distributed in the channels between the posts, and on the topof the posts having some small micro-channels. When exposed to heat(120° C.), the solvent (water) evaporated and the flatness of the firstsurface of the substrate was essentially restored leaving a regularpattern of the dye on the surface.

Example 20

A shape-memory substrate was made as described in Example 1 except thata 125 micrometers spacer was used. One of the surfaces of the substratewas deformed by pressing the sample between the metal tool (an array ofcube corners as described in U.S. Pat. No. 5,706,132, pyramidal heightof 87 micrometers), as described in Example 2. A border of adhesive wasmade on a plastic substrate and the microstructured surface was placedwithin and on the border. The retroreflectivity of the microstructuredsurface disappeared where in contact with the adhesive border, butremained retroreflective within the border.

The present invention should not be considered limited to the particularexamples described above, but rather should be understood to cover allaspects of the invention as fairly set out in the attached claims.Various modifications, equivalent processes, as well as numerousstructures to which the present invention may be applicable will bereadily apparent to those of skill in the art to which the presentinvention is directed upon review of the instant specification.

1. An article, comprising: a polymeric member including a surface havinga microstructure; and wherein the polymeric member comprises a shapememory polymer, the shape memory polymer comprising a copolymer networkcomprising the reaction product of a free radically polymerizablesiloxane having greater than one functional free radically polymerizablegroup and at least one (meth)acrylate monomer, wherein the at least one(meth)acrylate monomer, when homopolymerized, forms a homopolymer havinga glass transition temperature, a melting temperature, or both greaterthan about 40° C.
 2. The article of claim 1, wherein the free radicallypolymerizable siloxane has a number average molecular weight of about1,000-200,000 grams per mole.
 3. The article of claim 1, wherein thefree radically polymerizable siloxane includes a telechelic siloxane. 4.The article of claim 2, wherein the telechelic siloxane includes(meth)acryloxyurea siloxane.
 5. The article of claim 2, wherein thetelechelic siloxane includes acrylamidoamido siloxane.
 6. The article ofclaim 2, wherein the telechelic siloxane includes methacrylamidoamidosiloxane.
 7. The article of claim 2, wherein the telechelic siloxaneincludes methylstyrylurea siloxane.
 8. The article of claim 1, whereinthe (meth)acrylate monomer includes isobornyl acrylate.
 9. The articleof claim 1, wherein the copolymer network includes about 10-70weight-percent of the free radically polymerizable siloxane.
 10. Thearticle of claim 1, wherein the copolymer network includes about 10-60weight-percent of the free radically polymerizable siloxane.
 11. Thearticle of claim 1, wherein the copolymer network includes about 20-60weight-percent of the free radically polymerizable siloxane.
 12. Thearticle of claim 1, wherein the polymeric member includes a secondarysurface having a microstructure.
 13. An article, comprising: a polymericmember including a microstructured surface, wherein the microstructuredsurface includes a surface feature that is not visible to an unaidedeye; and wherein the polymeric member includes a shape memory polymer.14. The article of claim 13, wherein the shape memory polymer comprisesa copolymer network comprising the reaction product of a free radicallypolymerizable siloxane having greater than one functional free radicallypolymerizable group and at least one (meth)acrylate monomer, wherein theat least one (meth)acrylate monomer, when homopolymerized, forms ahomopolymer having a glass transition temperature, a meltingtemperature, or both greater than about 40° C.
 15. The article of claim14, wherein the free radically polymerizable siloxane has a numberaverage molecular weight of about 1,000-200,000 grams per mole.
 16. Thearticle of claim 14, wherein the (meth)acrylate monomer includesisobornyl acrylate.
 17. The article of claim 14, wherein the freeradically polymerizable siloxane includes a telechelic siloxane.
 18. Thearticle of claim 17, wherein the telechelic siloxane includes(meth)acryloxyurea siloxane, acrylamidoamido siloxane,methacrylamidoamido siloxane, or methylstyrylurea siloxane.
 19. Thearticle of claim 13, wherein the surface feature includes a plurality ofdepressions.
 20. The article of claim 13, wherein the surface featureincludes a plurality of projections.
 21. The article of claim 13,wherein the polymeric member includes a secondary surface having amicrostructure.
 22. An article, comprising: a polymeric member includinga microstructured surface, wherein the microstructured surface includesa surface feature that is not visible to an unaided eye; and wherein thepolymeric member includes a shape memory polymer, the shape memorypolymer comprising a copolymer network comprising the reaction productof (meth)acryloxyurea siloxane and isobornyl acrylate.
 23. An articlecomprising a shape memory polymer having a microstructured surface andcomprising a copolymer network, the copolymer network comprising thereaction product of a free radically polymerizable siloxane havinggreater than one functional free radically polymerizable group and atleast one (meth)acrylate monomer, wherein the at least one(meth)acrylate monomer, when homopolymerized, forms a homopolymer havinga glass transition temperature greater than about 40° C.